HS221 brazing brass rod,Brass welding rod 2.4mm
HS221 tin brass welding rod
Good wear resistance
Excellent corrosion resistance
High intensity.
Suface clean, Good smooth
HS221 brazing brass rod,Brass welding rod 2.4mm
HS221 brazing brass rod,Brass welding rod 2.4mm
HS221 brazing brass rod,Brass welding rod 2.4mm
Applications:
Brass Gas Welding Rods is suitable for gas-flame brazing, high temperature brazing of copper and
copper alloys, nickel, cast iron and hard alloys
HS221 brazing brass rod,Brass welding rod 2.4mm
During the brazing process, the filler metal flows into the joints between closely-fitting workpieces (base materials)
through capillary action. This is the ability of liquid to flow in a narrow space.
Without resorting to or resisting external forces such as gravity. Then make the filler metal slightly higher
than its melting point, and at the same time receive the flux,
Chemical cleaning and cleaning agent protection. It then flows through the workpiece (also known as wetting)
and is then cooled to connect the workpieces together.
HS221 brazing brass rod,Brass welding rod 2.4mm
Packing:
HS221 brazing brass rod,Brass welding rod 2.4mm
Clinets feedback:
HS221 brazing brass rod,Brass welding rod 2.4mm
You may like:
HS221 tin brass welding rod
Good wear resistance
Excellent corrosion resistance
High intensity.
Suface clean, Good smooth
HS221 brazing brass rod,Brass welding rod 2.4mm
| Type | Main Components | Melting Temperature | Corresponds to Standard of Foreign Countries | |
| AWS | DIN | |||
| L104 | Cu-Zn37-Si0.5-Sn0.4-Ni0.4 | 858-875 | ERCu | CuSn |
| L105 | Cu-Zn38-Mn4 | 880-909 | ||
| S201 | Cu-Sn1-Si0.3-Mn0.3 | 1030-1050 | ||
| S211 | Cu-Si3-Mn1 | 971-1026 | ERCuSi-A | CuSi3 |
| S213 | Cu-Sn8-P0.2 | 996 | ERCuSn-C | CuSn6 |
| S221 | Cu-Zn39-Sn1-Si0.2 | 890-905 | RBCuZn-A | |
| S222 | Cu-Zn40-Fe1-Sn0.8-Si0.1 | 865-890 | RBCuZn-C | L-CuZn39Sn |
| S225 | Cu-Zn48-Ni10-Si0.2 | 921-935 | RBCuZnNi-D | L-CuNi10Zn42 |
HS221 brazing brass rod,Brass welding rod 2.4mm
| Standard | Alloy | Chemical Composition(%) | Melting Range | Application | |
| Solidus | Liquidus | ||||
| AWS A5.8 BS EN14640 | RBCuZn-A CuZn40 | Cu:59 Sn:0.6 Zn:Bal. Other:0.5 | 886°C | 901°C | Braze welding of copper,steel and cast iron. |
| AWS A5.8 BS EN14640 | RBCuZn-B CuZnNi | Cu:58 Fe:0.7 Si:0.1 Mn:0.5 Ni:0.5 Sn:1.0 Zn:Bal. Other:0.5 | 866°C | 882°C | Gas welding and carbon arc welding of brass,also braze welding of copper,steel and cast iron. |
| AWS A5.8 | RBCuZn-C | Cu:58 Fe:0.7 Si:01 Mn:0.5 Sn:1.0 Zn:Bal. Other:0.5 | 866°C | 888°C | Gas welding and carbon arc welding of brass,also braze welding of copper,steel and cast iron. |
| AWS A5.8 BS EN14640 | RBCuZn-D CuZn40Ni10 | Cu:48 Si:0.1 Ni:10.0 P: Max0.25 Zn:Bal. Other:0.5 | 921°C | 935°C | Braze welding of steel, nickel and carbide alloys. |
| HS221 SW221 | Cu:59 Sn:1.0 Si:0.2 Zn:Bal. Other:0.5 | 875°C | 890°C | Gas welding and carbon arc welding of brass,also braze welding of copper,steel and cast iron. | |
HS221 brazing brass rod,Brass welding rod 2.4mm
Applications:
Brass Gas Welding Rods is suitable for gas-flame brazing, high temperature brazing of copper and
copper alloys, nickel, cast iron and hard alloys
HS221 brazing brass rod,Brass welding rod 2.4mm
During the brazing process, the filler metal flows into the joints between closely-fitting workpieces (base materials)
through capillary action. This is the ability of liquid to flow in a narrow space.
Without resorting to or resisting external forces such as gravity. Then make the filler metal slightly higher
than its melting point, and at the same time receive the flux,
Chemical cleaning and cleaning agent protection. It then flows through the workpiece (also known as wetting)
and is then cooled to connect the workpieces together.